Reinforcement of ribs

Yesterday and today we laminated the reinforcement of the ribs. We used 200 g/m² non-crimpt biaxial carbon fabrics and a covering layer of 100 g/m² flax fabrics. Biaxial carbon fabrics are great when you have corners. The stiff carbon fibers have then an orientation of ±45°, so that the fibers are bent less and wrapping them around the corner is much easier. Also, this orientation is optimal for shear loads.

P1080400_mP1080401_m

You might ask why we used flax fabrics. Well, they protect the load-bearing carbon fibers from external abrasion! Flax behaves much like aramid (Nomex® and co.): It takes some energy until it is damaged. Such a covering protects not only the load-bearing fibers, but also the pilot from sharp edges.

The reinforcements are curing now in vacuum at roughly 200 mbar residual pressure. The surplus resin is taken up by breather felt. We used also a covering layer of peel ply to obtain again a rough surface.

P1080402_m

P1080403_m

Advertisements

Kommentar verfassen

Trage deine Daten unten ein oder klicke ein Icon um dich einzuloggen:

WordPress.com-Logo

Du kommentierst mit Deinem WordPress.com-Konto. Abmelden / Ändern )

Twitter-Bild

Du kommentierst mit Deinem Twitter-Konto. Abmelden / Ändern )

Facebook-Foto

Du kommentierst mit Deinem Facebook-Konto. Abmelden / Ändern )

Google+ Foto

Du kommentierst mit Deinem Google+-Konto. Abmelden / Ändern )

Verbinde mit %s